PVDF coating, made of fluorine carbon resin, is solidified into a dry film with super-weather resistance. After 2-3 coats and baking, the warranty could reach 15–20 years for exterior use.
It has excellent weather resistance, strong corrosion resistance, high surface hardness, and good wear resistance. For more information, please click here.
PVDF coating can resist ultraviolet light, acid rain, air pollution, and other erosion for a long time, and keeps the color and luster stable.
Strong corrosion resistance can be used in harsh environments. High surface hardness and good wear resistance. For example, when often used in the exterior wall decoration of high-rise buildings, long-term exposure to the outdoors can still maintain a good appearance.
The color chips in this guide are reproduced as closely as possible to paint colors and to be used only as a guide.
| SPRAY WayPower | |
| Minimum Dry Film Thickness Requirements | |
| Metal 3-Coat Color | |
| Inhibitive Primer | 7.5μm+2.5μ |
Metallic Color Top Coat | 27.5μm+2.5μ |
Clear Top Coat | 12.5μm+2.5μ |
Total Minimum Requirements | 40.0μ |
| 2 Coating Plain Color | 2 Coated Metallic Colors | ||
| SPRAY WayPower | SPRAY WayPowe | ||
| Minimum Dry Film Thickness Requirements | Minimum Dry Film Thickness Requirements | ||
| Metal 2-Coat Color | Metal 2-Coat Color | ||
| Inhibitive Primer | 7.5μm+2.5μ | Inhibitive Primer | 10μm+2.5μ |
| Metallic Color Top Coat | 27.5μm+2.5μ | Metallic Color Top Coat | 30μm+2.5μ |
| Total Minimum Requirements | 30.0μ | Total Minimum Requirements | 35.0μ |
| AAMA 2605-05 | ||||
| for High Performance Organic Coatings on Alumnium Extrusion and Panels | ||||
| Description | Coatings Requirements | WayPower Performance | ||
| Color Uniformity | Visual Control | Instrument and Visually controlled | ||
| Specular gloss at 60°ASTMD 523 | Medium and low gloss ranges | Controlled to custom spec ±5units | ||
| Dry film hardness, ASTM D3363 | Fminimum | H-2H | ||
| Film adhesion(dry,wet and boiling water),crosshatch 1/16 inch squares 1/16" | No removal between scribed lines | No removal | ||
| Impact resistance(direct),0.10 inchdistortion | No removal of film | No removal | ||
| Abrasion resistance, ASTMD 968 | 20 liters per mil | Exceeds spec | ||
| Chemical resistance（10% murfaticacid） | 15 minutes, no visual changes | Meets or exceeds spec | ||
| Chemical resistance(mortar,alkali) | 24 hours no visual changes | Meets or exceeds spec | ||
| Resistance to acid pollutants(70% nitric) | 30 minutes, maximum 5ΔENBSunits color change | Meets or exceeds spec | ||
| Detergent resistance | 72hours,no effect | Meets or exceeds spec | ||
| Humidity resistance, ASTMD 2247 | 4000hours,few#8 blisters(maximum) | Meets or exceeds spec | ||
| Salt spray resistance, ASTMB 117 | 4000hours, minimum 7 rating onscribe and minimum blisterating of 8(ASTMD 1654) | Meets or exceeds spec | ||
| Weathering, color retention, ASTMD2244 | 10 years,45° South Florida,maximum5ΔENBS units color change | Meets or exceeds spec | ||
| Weathering, chalk retention, ASTMD4214 | 10 years,45°South Florida,8 ratingfor colors,6 rating for whites | Meets or exceeds spec | ||
| Weathering, erosion resistance | 10 years,45° South Florida,maximum 20%loss | Meets or exceeds spec | ||